Product Details:
| Brand | Mobil |
| NLGI Grade | 2 |
| Thickener Type | Polyurea |
| Water Washout | 5, 79Deg C, ASTM D1264, % Weight Loss |
| Color | White |
| Penetration | 280, Worked, 25 Deg C, ASTM D217, 0.1 mm |
| Dropping Point | 270, ASTM D2265, DegC |
| Water Spray | 30, Off, ASTM D4049, % Weight Loss |
| Four Ball Wear | 0.45, ASTM D 2266, Scar, mm |
| Four Ball Weld Point | 400, ASTM D 2596, kg |
| Bearing Corrosion | Pass ASTM D 1743, Rating |
| EMCOR Rust Test | Distilled Water, Rating, 0, ASTM D6138 |
| Grease Life | 350, 160Deg C, DIN 51821-160, F50, Hours |
| Pumpability | 7, 18Deg C, USS DM-43, g/minute |
The Mobil SHC™ Polyrex series of greases are specifically designed to improve your productivity by solving high-temperature lubrication problems in both general industry and food processing applications. Developed using advanced Polyurea technology, these synthetic, polymer-enhanced greases bring a high-temperature solution to the market while carrying a full NSF H1 registration.
The Mobil SHC Polyrex Series of greases are designed to offer a combination of high-temperature performance, excellent water resistance, and the balanced wear performance consistent with Mobil grease products. Using advanced Polyurea thickener technology, ExxonMobil researchers developed a unique combination of synthetic oils that achieve excellent high-temperature performance able to provide lubrication up to 170°C. Even at these extreme temperatures, Mobil SHC Polyrex resists oxidation and loss of structural stability allowing re-lubrication intervals to be extended while maintaining equipment protection. The carefully balanced combination of thickener, base oils, and additives yields a grease with excellent load carrying capabilities and rust protection. Mobil SHC Polyrex is also highly resistant to water and has excellent corrosion protection providing added protection to equipment in wet, humid environments and applications where water wash downs are frequent.
The Mobil brand of oils and greases is recognized around the world for its innovation and outstanding performance. Mobil SHC Polyrex utilizes the advanced thickener technology of the Mobil Polyrex family of greases to deliver a high performance, problem-solving product for some of industries toughest lubrication problems. Mobil SHC Polyrex brings that performance to another level through the addition of a unique combination of synthetic oils, polymer enhancement and a balanced additive package that is geared to deliver solutions to tough lubrication problems.
Application Considerations: While Mobil SHC Polyrex Series greases are compatible with many Polyurea and lithium complex greases, admixture may detract from their performance. Consequently it is recommended that before changing a system to one of the Mobil SHC Polyrex greases, it should be thoroughly cleaned out to achieve the maximum performance benefits. While the Mobil SHC Polyrex greases share many performance benefits, their applications are best described in terms of each product grade:
Product Details:
| Brand | Mobil |
| Thickener Type | Polyurea |
| Water Washout | 7, 79Deg C, ASTM D1264, % Weight Loss |
| Color | White |
| Penetration | 280, Worked, 25 Deg C, ASTM D217, 0.1 mm |
| Dropping Point | 260, ASTM D2265, DegC |
| Water Spray | 28, Off, ASTM D4049, % Weight Loss |
| Four Ball Wear | 0.45, ASTM D 2266, Scar, mm |
| Four Ball Weld Point | 400, ASTM D 2596, kg |
| Bearing Corrosion | Pass ASTM D 1743, Rating |
| EMCOR Rust Test | Rating, 0, ASTM D6138, Distilled Water |
| Grease Life | 350, 160Deg C, DIN 51821-160, F50, Hours |
| Pumpability | 18, 18Deg C, USS DM-43, g/minute |
The Mobil SHC™ Polyrex series of greases are specifically designed to improve your productivity by solving high-temperature lubrication problems in both general industry and food processing applications. Developed using advanced Polyurea technology, these synthetic, polymer-enhanced greases bring a high-temperature solution to the market while carrying a full NSF H1 registration.
The Mobil SHC Polyrex Series of greases are designed to offer a combination of high-temperature performance, excellent water resistance, and the balanced wear performance consistent with Mobil grease products. Using advanced Polyurea thickener technology, ExxonMobil researchers developed a unique combination of synthetic oils that achieve excellent high-temperature performance able to provide lubrication up to 170°C. Even at these extreme temperatures, Mobil SHC Polyrex resists oxidation and loss of structural stability allowing re-lubrication intervals to be extended while maintaining equipment protection. The carefully balanced combination of thickener, base oils, and additives yields a grease with excellent load carrying capabilities and rust protection. Mobil SHC Polyrex is also highly resistant to water and has excellent corrosion protection providing added protection to equipment in wet, humid environments and applications where water wash downs are frequent.
The Mobil brand of oils and greases is recognized around the world for its innovation and outstanding performance. Mobil SHC Polyrex utilizes the advanced thickener technology of the Mobil Polyrex family of greases to deliver a high performance, problem-solving product for some of industries toughest lubrication problems. Mobil SHC Polyrex brings that performance to another level through the addition of a unique combination of synthetic oils, polymer enhancement and a balanced additive package that is geared to deliver solutions to tough lubrication problems.
Application Considerations: While Mobil SHC Polyrex Series greases are compatible with many Polyurea and lithium complex greases, admixture may detract from their performance. Consequently it is recommended that before changing a system to one of the Mobil SHC Polyrex greases, it should be thoroughly cleaned out to achieve the maximum performance benefits. While the Mobil SHC Polyrex greases share many performance benefits, their applications are best described in terms of each product grade:
Product Details:
| Brand | Mobil |
| NLGI Grade | 1 |
| Thickener Type | Polyurea |
| Water Washout | 7, 79Deg C, ASTM D1264, % Weight Loss |
| Color | White |
| Viscosity | ASTM D 445 |
| Penetration | 325, Worked, 25 Deg C, ASTM D217, 0.1 mm |
| Dropping Point | 270, ASTM D2265, DegC |
| Four Ball Wear | 0.45, ASTM D 2266, Scar, mm |
| Four Ball Weld Point | 400, ASTM D 2596, kg |
| Bearing Corrosion | Pass ASTM D 1743, Rating |
| EMCOR Rust Test | ASTM D6138, 0, Rating, Distilled Water |
| Pumpability | 30, 18Deg C, USS DM-43, g/minute |
The Mobil SHC™ Polyrex series of greases are specifically designed to improve your productivity by solving high-temperature lubrication problems in both general industry and food processing applications. Developed using advanced Polyurea technology, these synthetic, polymer-enhanced greases bring a high-temperature solution to the market while carrying a full NSF H1 registration.
The Mobil SHC Polyrex Series of greases are designed to offer a combination of high-temperature performance, excellent water resistance, and the balanced wear performance consistent with Mobil grease products. Using advanced Polyurea thickener technology, ExxonMobil researchers developed a unique combination of synthetic oils that achieve excellent high-temperature performance able to provide lubrication up to 170°C. Even at these extreme temperatures, Mobil SHC Polyrex resists oxidation and loss of structural stability allowing re-lubrication intervals to be extended while maintaining equipment protection. The carefully balanced combination of thickener, base oils, and additives yields a grease with excellent load carrying capabilities and rust protection. Mobil SHC Polyrex is also highly resistant to water and has excellent corrosion protection providing added protection to equipment in wet, humid environments and applications where water wash downs are frequent.
The Mobil brand of oils and greases is recognized around the world for its innovation and outstanding performance. Mobil SHC Polyrex utilizes the advanced thickener technology of the Mobil Polyrex family of greases to deliver a high performance, problem-solving product for some of industries toughest lubrication problems. Mobil SHC Polyrex brings that performance to another level through the addition of a unique combination of synthetic oils, polymer enhancement and a balanced additive package that is geared to deliver solutions to tough lubrication problems.
Application Considerations: While Mobil SHC Polyrex Series greases are compatible with many Polyurea and lithium complex greases, admixture may detract from their performance. Consequently it is recommended that before changing a system to one of the Mobil SHC Polyrex greases, it should be thoroughly cleaned out to achieve the maximum performance benefits. While the Mobil SHC Polyrex greases share many performance benefits, their applications are best described in terms of each product grade:
Product Details:
| Brand | Mobil |
| NLGI Grade | 00 |
| Thickener Type | Polyurea |
| Water Washout | 37, 79Deg C, ASTM D1264, % Weight Loss |
| Color | White |
| Penetration | 415, Worked, 25 Deg C, ASTM D217, 0.1 mm |
| Dropping Point | 260, ASTM D2265, DegC |
| Four Ball Wear | 0.45, ASTM D 2266, Scar, mm |
| Four Ball Weld Point | 400, ASTM D 2596, kg |
| Bearing Corrosion | Pass |
| EMCOR Rust Test | 0, Distilled Water, ASTM D6138, Rating |
| Pumpability | 40, 18Deg C, USS DM-43, g/minute |
The Mobil SHC™ Polyrex series of greases are specifically designed to improve your productivity by solving high-temperature lubrication problems in both general industry and food processing applications. Developed using advanced Polyurea technology, these synthetic, polymer-enhanced greases bring a high-temperature solution to the market while carrying a full NSF H1 registration.
The Mobil SHC Polyrex Series of greases are designed to offer a combination of high-temperature performance, excellent water resistance, and the balanced wear performance consistent with Mobil grease products. Using advanced Polyurea thickener technology, ExxonMobil researchers developed a unique combination of synthetic oils that achieve excellent high-temperature performance able to provide lubrication up to 170°C. Even at these extreme temperatures, Mobil SHC Polyrex resists oxidation and loss of structural stability allowing re-lubrication intervals to be extended while maintaining equipment protection. The carefully balanced combination of thickener, base oils, and additives yields a grease with excellent load carrying capabilities and rust protection. Mobil SHC Polyrex is also highly resistant to water and has excellent corrosion protection providing added protection to equipment in wet, humid environments and applications where water wash downs are frequent.
The Mobil brand of oils and greases is recognized around the world for its innovation and outstanding performance. Mobil SHC Polyrex utilizes the advanced thickener technology of the Mobil Polyrex family of greases to deliver a high performance, problem-solving product for some of industries toughest lubrication problems. Mobil SHC Polyrex brings that performance to another level through the addition of a unique combination of synthetic oils, polymer enhancement and a balanced additive package that is geared to deliver solutions to tough lubrication problems.
Application Considerations: While Mobil SHC Polyrex Series greases are compatible with many Polyurea and lithium complex greases, admixture may detract from their performance. Consequently it is recommended that before changing a system to one of the Mobil SHC Polyrex greases, it should be thoroughly cleaned out to achieve the maximum performance benefits. While the Mobil SHC Polyrex greases share many performance benefits, their applications are best described in terms of each product grade:
Product Details:
| Brand | Mobil |
| Application | Industrial |
| Packing | Bucket |
| NLGI Grade | 2 |
| Water Washout | 1.0, ASTM D 1264, % |
| Rust Protection | Pass, ASTM D 1743, Distilled Water |
| Color | Red |
| CST | 87, 10.7, @ 40 DegC, @ 100 DegC |
| Running | 297 |
| EMCOR Corrosion Performance | 10% Synthetic Sea Water ASTM D 6138 (Prepared As Per ASTM D 665B), 0 |
| Copper Corrosion Resistance | 1A, ASTM D 4048 |
| Viscosity Index | 108, ASTM D 2270 |
| Penetration | 270, ASTM D217 worked, 60x, mm/10 |
| Penetration Change | 16, after 100.000 strokes, ASTM D217, mm/10 |
| Dropping Point | 253, ASTM D 2265, Deg C (Deg F) |
| Four Ball Wear Scar | 0.49, ASTM D 2266, @ 40kg, 1200 rpm, 75 Deg C, 1 hr, mm |
| Oil separation Test | 0.0, ASTM D 1742, % |
| Low Temperature Torque | ASTM D 1478, g-cm @ -29 Deg C |
| Starting | 2210 |
High-Performance Mobil SHC™ Polyrex EM Series greases are specially formulated for electric-motor bearings. The advanced thickener formulation and proprietary manufacturing techniques provide improved bearing performance and protection for long electric motor life.
Mobil SHC Polyrex 102 EM Series has demonstrated up to 40% improvement in bearing torque reduction in controlled laboratory testing(*).
The energy efficiency design is a trademark of Exxon Mobil Corporation.
(*) Torque reduction relates solely to the performance of Mobil SHC Polyrex 102 EM when compared to conventional (mineral) reference grease of a similar viscosity grade in a deep grove ball bearing. The technology used allows up to 40 % torque reduction compared to the reference when tested in a bearing under controlled conditions. Efficiency improvements will vary based on operating conditions and equipment.
Mobil SHC Polyrex 102 EM and Mobil SHC Polyrex 103 EM offer the following features and benefits:
Applications:
Mobil SHC Polyrex 102 EM greases are recommended by major bearing and electric motor manufacturers for long-life lubrication of electric motor ball and roller bearings.
Mobil SHC Polyrex 103 EM is more specifically recommended for applications such as vertically mounted bearings, or very large motors where a stiffer grease consistency may be required by the OEM, and low noise properties are not required.
Mobil SHC Polyrex EM greases have been shown to be compatible with a number of ExxonMobil lithium complex greases, as well as competitive electric motor mineral polyurea products, as determined by the methodology of ASTM D6185. For specific questions about grease compatibility, contact your Mobil representative.
Key applications include:
Product Details:
| Application | Industrial |
| Packing | Bucket |
| NLGI Grade | 3 |
| Water Washout | 0.4, ASTM D 1264, % |
| Rust Protection | Pass, ASTM D 1743, Distilled Water |
| Color | Red |
| Base Oil Viscosity | ASTM D 445 |
| Running | 313 |
| EMCOR Corrosion Performance | 10% Synthetic Sea Water ASTM D 6138 (Prepared As Per ASTM D 665B), 0 |
| Copper Corrosion Resistance | 1A, ASTM D 4048 |
| CST | 87, 10.7, @ 40 DegC, @ 100 DegC |
| Penetration | 238, ASTM D217 worked, 60x, mm/10 |
| Penetration Change After | 23, 100.000 strokes, ASTM D217, mm/10 |
| Dropping Point | 269, ASTM D 2265, Deg C (Deg F) |
| Four Ball Wear Scar | 0.60, ASTM D 2266, @ 40kg, 1200 rpm, 75 Deg C, 1 hr, mm |
| Oil Separation Test | 0.1, ASTM D 1742, % |
| Low Temperature Torque | ASTM D 1478, g-cm @ -29 Deg C |
| Starting | 3270 |
High-Performance Mobil SHC™ Polyrex EM Series greases are specially formulated for electric-motor bearings. The advanced thickener formulation and proprietary manufacturing techniques provide improved bearing performance and protection for long electric motor life.
Mobil SHC Polyrex 102 EM Series has demonstrated up to 40% improvement in bearing torque reduction in controlled laboratory testing(*).
The energy efficiency design is a trademark of Exxon Mobil Corporation.
(*) Torque reduction relates solely to the performance of Mobil SHC Polyrex 102 EM when compared to conventional (mineral) reference grease of a similar viscosity grade in a deep grove ball bearing. The technology used allows up to 40 % torque reduction compared to the reference when tested in a bearing under controlled conditions. Efficiency improvements will vary based on operating conditions and equipment.
Mobil SHC Polyrex 102 EM and Mobil SHC Polyrex 103 EM offer the following features and benefits:
Applications:
Mobil SHC Polyrex 102 EM greases are recommended by major bearing and electric motor manufacturers for long-life lubrication of electric motor ball and roller bearings.
Mobil SHC Polyrex 103 EM is more specifically recommended for applications such as vertically mounted bearings, or very large motors where a stiffer grease consistency may be required by the OEM, and low noise properties are not required.
Mobil SHC Polyrex EM greases have been shown to be compatible with a number of ExxonMobil lithium complex greases, as well as competitive electric motor mineral polyurea products, as determined by the methodology of ASTM D6185. For specific questions about grease compatibility, contact your Mobil representative.
Key applications include:
Product Details:
| Brand | Mobil |
| NLGI Grade | 2 |
| Water Washout | 1.9, ASTM D 1264, % |
| Rust Protection | Pass, ASTM D 1743, Distilled Water |
| Color | Blue |
| CST | 115, 12.2, @ 40 Deg C, @ 100 Deg C |
| Copper Corrosion Resistance | 1A, ASTM D 4048 |
| Viscosity Index | 95, ASTM D 2270 |
| Penetration | 285, ASTM D217 worked, 60x, mm/10 |
| Penetration Change After | 40, 100.000 strokes, ASTM D217, mm/10 |
| Dropping Point | 260, ASTM D 2265, Deg C ( Deg F) |
| Oil Separation Test | 0.5, ASTM D 1742, % |
| High Temperature Grease Life | 750+, ASTM D 3336, Hours @ 177 Deg C |
| Four Ball Wear Scar | 0.41, ASTM D 2266, @ 40kg, 1200 rpm, 75n Deg C, 1 hr, mm |
| Starting | 7500 |
Super-premium Mobil Polyrex™ EM Series greases are specially formulated for electric-motor bearings. The advanced thickener formulation and proprietary manufacturing techniques provide improved bearing performance and protection for long electric motor life.
Features and Benefits:
Mobil Polyrex EM and Mobil Polyrex EM 103 offer the following features and benefits:
| Features | Advantages and Potential Benefits |
| Outstanding grease life | Outstanding long-life, high-temperature lubrication of ball and roller bearings, particularly in sealed-for-life applications |
| Advanced polyurea thickener | Increased durability versus conventional polyurea greases when subjected to mechanical shear forces |
| Excellent corrosion resistance | Mobil Polyrex EM and Mobil Polyrex EM 103 provide protection against rust and corrosion.Mobil Polyrex EM provides additional protection under mild salt-water wash conditions versus Polyrex EM 103 |
| Low-noise properties | Mobil Polyrex EM is suitable for lubrication of ball bearings in many noise-sensitive applications |
Mobil Polyrex EM greases are recommended by many major bearing and electric motor manufacturers for long-life lubrication of electric motor ball and roller bearings.
Mobil Polyrex EM 103 is more specifically recommended for applications such as vertically mounted bearings, or very large motors where a stiffer grease consistency may be required by the OEM.
Mobil Polyrex EM greases have been shown to be compatible with a number of ExxonMobil lithium complex greases, as well as competitive electric motor mineral polyurea products, as determined by the methodology of ASTM D6185. For specific questions about grease compatibility, contact your Mobil representative.
Key applications include:
Product Details:
| Brand | Mobil |
| Application | Automotive, Industrial |
| NLGI Grade | 3 |
| Water Washout | 0.8, ASTM D 1264, % |
| Rust Protection | Pass, ASTM D 1743, Distilled Water |
| Color | Blue |
| CST | 115, 12.2, @ 40 DegC, @ 100 DegC |
| Running | 1000 |
| Copper Corrosion Resistance | 1A, ASTM D 4048 |
| Viscosity Index | 95, ASTM D 2270 |
| Penetration | 250, ASTM D217 worked, 60x, mm/10 |
| Penetration Change After | 40, 100.000 strokes, ASTM D217, mm/10 |
| Dropping Point | 270, ASTM D2265, Deg C |
| Oil Separation Test | 0.1, ASTM D 1742, % |
| High Temperature Grease Life | 750+, ASTM D 3336, Hours @ 177 Deg C |
| Four Ball Wear Scar | 0.6, ASTM D 2266, @ 40kg, 1200 rpm, 75 Deg C, 1 hr, mm |
| Starting | 9300 |
Super-premium Mobil Polyrex™ EM Series greases are specially formulated for electric-motor bearings. The advanced thickener formulation and proprietary manufacturing techniques provide improved bearing performance and protection for long electric motor life.
Features and Benefits:
Mobil Polyrex EM and Mobil Polyrex EM 103 offer the following features and benefits:
| Features | Advantages and Potential Benefits |
| Outstanding grease life | Outstanding long-life, high-temperature lubrication of ball and roller bearings, particularly in sealed-for-life applications |
| Advanced polyurea thickener | Increased durability versus conventional polyurea greases when subjected to mechanical shear forces |
| Excellent corrosion resistance | Mobil Polyrex EM and Mobil Polyrex EM 103 provide protection against rust and corrosion.Mobil Polyrex EM provides additional protection under mild salt-water wash conditions versus Polyrex EM 103 |
| Low-noise properties | Mobil Polyrex EM is suitable for lubrication of ball bearings in many noise-sensitive applications |
Mobil Polyrex EM greases are recommended by many major bearing and electric motor manufacturers for long-life lubrication of electric motor ball and roller bearings.
Mobil Polyrex EM 103 is more specifically recommended for applications such as vertically mounted bearings, or very large motors where a stiffer grease consistency may be required by the OEM.
Mobil Polyrex EM greases have been shown to be compatible with a number of ExxonMobil lithium complex greases, as well as competitive electric motor mineral polyurea products, as determined by the methodology of ASTM D6185. For specific questions about grease compatibility, contact your Mobil representative.
Key applications include: